Methods for manufacturing semiconductor devices and semiconductor devices

ABSTRACT

Embodiments of the present invention include a method for manufacturing a semiconductor device, in which, when a DRAM and a MOS field effect transistor that becomes a component of a logic circuit are mix-mounted on the same chip, the DRAM and the MOS field effect transistor can be provided with designed performances. After a capacitor  700  of the DRAM is formed, silicide layers  19   a  and  19   b  are formed over N +  type source/drain regions  41   c  and  41   d  of MOS field effect transistors  200   c   , 200   d  and  200   e  that are located in peripheral circuit region  2000  and logic circuit region  3000.

REFERENCE TO CROSS-RELATED APPLICATIONS

Japanese patent application no. 2000-5042, filed Jan. 13, 2000, is hereby incorporated by reference in its entirety. U.S. patent application Ser. No. 09/759,666, filed on Jan. 13, 2001, is hereby incorporated by reference in its entirety. U.S. patent application Ser. No. 09/759,915, filed on Jan. 13, 2001, is hereby incorporated by reference in its entirety. U.S. patent application Ser. No. 09/759,715, filed on Jan. 13, 2001, is hereby incorporated by reference in its entirety.

TECHNICAL FIELD

The present invention relates to methods for manufacturing semiconductor devices that mix-mount DRAMs (Dynamic Random Access Memories) and other device elements in the same chip, and semiconductor devices manufactured thereby.

BACKGROUND

In recent years, the mixed-mounting of various types of circuits is required in consideration of various factors, such as, for example, to shorten the chip interface delay, to reduce the cost per board area, and to reduce the cost in design and development of boards. There are problems in the mix-mounting technology in that the process becomes complex and the IC cost increases.

SUMMARY

One embodiment of the present invention relates to a method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region. The method includes (a) forming a capacitor for the DRAM; and (b) after step (a), forming a silicide layer at a source/drain region of the field effect transistor.

Another embodiment relates to a method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region, a first field effect transistor that is located in a peripheral circuit region and becomes a component of a peripheral circuit for the DRAM, and a second field effect transistor located in a region other than the memory cell region and the peripheral circuit region. The method includes (A) forming the first field effect transistor with a source/drain that does not have a silicide layer in the peripheral circuit region. Step (B), after step (A), includes forming a capacitor for the DRAM. Step (C), after step B, includes forming a silicide layer at a source/drain of the second field effect transistor.

Another embodiment relates to a semiconductor device including a DRAM located in a memory cell region, and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region. The device also includes silicide layers formed at a cell plate that is a component of a capacitor of the DRAM and at a source/drain that is a component of the field effect transistor. In addition, silicide layers are not formed at a source/drain that is a component of a memory cell selection field effect transistor of the DRAM.

Another embodiment relates to a semiconductor device including a DRAM located in a memory cell region. The device also includes a first field effect transistor that is located in a peripheral circuit region and becomes a component of a peripheral circuit for the DRAM, and a second field effect transistor located in a region other than the memory cell region and the peripheral circuit region. The device also includes silicide layers formed at a cell plate that is a component of a capacitor of the DRAM and at a source/drain of the second field effect transistor. In addition, silicide layers are not formed at a source/drain that is a component of a memory cell selection field effect transistor of the DRAM or at a source/drain of the first field effect transistor.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the invention are described with reference to the accompanying drawings which, for illustrative purposes, are schematic and not necessarily drawn to scale.

FIG. 1 schematically shows a cross section of a silicon substrate, which is used to describe a first step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 2 schematically shows a cross section of the silicon substrate, which is used to describe a second step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 3 schematically shows a cross section of the silicon substrate, which is used to describe a third step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 4 schematically shows a cross section of the silicon substrate, which is used to describe a fourth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 5 schematically shows a cross section of the silicon substrate, which is used to describe a fifth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 6 schematically shows a cross section of the silicon substrate, which is used to describe a sixth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 7 schematically shows a cross section of the silicon substrate, which is used to describe a seventh step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 8 schematically shows a cross section of the silicon substrate, which is used to describe an eighth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 9 schematically shows a cross section of the silicon substrate, which is used to describe a ninth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 10 schematically shows a cross section of the silicon substrate, which is used to describe a tenth step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 11 schematically shows a cross section of the silicon substrate, which is used to describe an eleventh step in a method for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 12 schematically shows a cross section of the semiconductor device in accordance with the method as illustrated in FIGS. 1-11 for manufacturing a semiconductor device of an embodiment of the present invention.

FIG. 13 schematically shows a cross section of a silicon substrate, which is used to describe a modified embodiment of the present invention.

FIG. 14 schematically shows a cross section of a silicon substrate, which is used to describe another modified embodiment of the present invention.

FIG. 15 schematically shows a cross section of a silicon substrate, which is used to describe another modified embodiment of the present invention.

FIG. 16 schematically shows a cross section of a silicon substrate, which is used to describe a first step of another modified embodiment of the present invention.

FIG. 17 schematically shows a cross section of the silicon substrate, which is used to describe a second step of the modified embodiment of FIG. 16.

FIG. 18 schematically shows a cross section of the silicon substrate, which is used to describe a third step modified embodiment of FIGS. 16 and 17.

FIG. 19 schematically shows a cross section of the silicon substrate, which is used to describe a fourth step of the modified embodiment of FIGS. 16, 17 and 18.

DETAILED DESCRIPTION

Certain embodiments of the present invention to methods for manufacturing semiconductor devices having a DRAM and another element that are mounted on the same chip, which can provide the DRAM and the other element with designated performances, and semiconductor devices manufactured thereby.

One embodiment provides a method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; and after the step (a), (b) forming a silicide layer at a source/drain region of the field effect transistor.

By the method for manufacturing a semiconductor device including the above-described steps, a chip that mix-mounts a DRAM and a field effect transistor formed with a silicide at its source/drain is manufactured. In accordance with this embodiment, the capacitor for the DRAM is inhibited or prevented from being polluted by metals. The reasons therefor are described below.

For a higher speed of a field effect transistor, a silicide layer may be formed at source/drain of the field effect transistor. Through the step of forming the silicide layer, metals inevitably adhere to the semiconductor manufacturing apparatus. If the metals are contained in a dielectric layer of a capacitor, the characteristic of the capacitor deteriorates, which adversely affects the performance of the RAM. In accordance with certain embodiments of the present invention, after the capacitor for the DRAM is formed, the silicide layers are formed at the source/drain of the field effect transistor. Therefore, the metal-pollution of the capacitor is inhibited or prevented.

Also, in accordance with certain embodiments of the present invention, since the silicide layer is formed at the source/drain of the field effect transistor after the capacitor for the DRAM is formed, the resistance of the silicide layer is prevented from increasing. In other words, if the silicide layer were to be formed before the capacitor is formed, the silicide layer is affected by the heat generated during the formation of the capacitor, and therefore the resistance of the silicide layer increases.

It is noted that in certain embodiments, a field effect transistor region refers to a region other than a memory cell region. A field effect transistor located in a field effect transistor region defines a component of, for example, a logic circuit and a peripheral circuit for a DRAM (including a sense amplifier). The same definition applies to field effect transistors described below.

One example of a semiconductor device manufactured by an embodiment of the present invention is as follows. The semiconductor device is equipped with a DRAM located in a memory cell region, and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region. The semiconductor device is characterized in that silicide layer are formed at a cell plate that defines a component of a capacitor of the DRAM and at a source/drain that defines a component of the field effect transistor, but silicide layers are not formed at a source/drain that defines a component of a memory cell selection field effect transistor of the DRAM.

In certain embodiments of the present invention, a silicide layer is not formed at a source/drain that defines a component of a memory cell selection field effect transistor because of the following reasons. The leak current of the memory cell selection field effect transistor is a source of deterioration in the charge-retaining characteristic of a DRAM capacitor. In this respect, a reduced leak current is required more than a higher operation speed in a memory cell selection field effect transistor. If a silicide layer is formed at the source/drain of the memory cell selection field effect transistor, the leak current increases.

In a method for manufacturing a semiconductor device in accordance with the certain embodiments of present invention, the following steps may be added. Before the step (a) described above, the method includes the steps of (c) forming an etching stopper layer in the field effect transistor region, and (d) forming an interlayer dielectric layer in the memory cell region and the field effect transistor region, and further includes, between the step (a) and the step (b), the step of (e) removing the interlayer dielectric layer located in the field effect transistor region by an etching, using the etching stopper layer as an etching stopper.

In accordance with embodiments with the above-described steps being added, when the interlayer dielectric layer is removed by an etching, an underlying layer (for example, an element isolation insulation layer) is prevented from being cut in an area where the interlayer dielectric layer is relatively thin. In other words, in accordance with certain embodiments the present invention, a capacitor for the DRAM is formed after an interlayer dielectric layer is formed in the memory cell region. Since the interlayer dielectric layer is formed over the surface of the semiconductor substrate, it is also formed over the field effect transistor region. Therefore, before a silicide is formed, the interlayer dielectric layer located in the field effect transistor region needs to be removed. It is noted that variations in the thickness of the interlayer dielectric layer unavoidably occur, and areas of the interlayer dielectric layer that are thinner are etched and removed first, compared to areas thereof having a greater thickness. As a result, when the interlayer dielectric layer is removed, and if there is not an etching stopper layer below the interlayer dielectric layer, an underlying layer such as an element isolation insulation layer is etched in areas where the thickness of the interlayer dielectric layer are small. As a result, problems such as a lowered element isolation dielectric strength and the like occur. In accordance with certain embodiments of the present invention, an etching stopper layer is formed below the interlayer dielectric layer. As a result, when the interlayer dielectric layer is removed, an underlying layer such as an element isolation insulation layer in areas where the thickness of the interlayer dielectric layer are small can be inhibited or prevented from being etched.

In a method for manufacturing a semiconductor device in accordance with certain embodiments of the present invention, the following steps may be added. After the step (b), the method includes the steps of (f) forming another interlayer dielectric layer in the memory cell region and the field effect transistor region, and (g) polishing the other interlayer dielectric layer by CMP (chemical mechanical polishing) to thereby planarize the other interlayer dielectric layer.

In accordance with certain embodiments of the present invention with the above-described steps being added, the other interlayer dielectric layer is planarized by a CMP method, with the result that the reliability of a wiring layer to be formed over the other interlayer dielectric layer can be improved.

In a method for manufacturing a semiconductor device in accordance with certain embodiments of the present invention, the following steps may be added. After the step (b), the method may include the steps of (f) forming another interlayer dielectric layer in the memory cell region and the field effect transistor region, and (g) photo-etching the other interlayer dielectric layer located in the memory cell region to thereby planarize the other interlayer dielectric layer. Photo-etching refers to the deposition of photoresist, then exposure to form a pattern, and then etching, as known in the art.

In accordance with embodiments of the present invention with the above-described steps being added, the other interlayer dielectric layer is planarized by an etchback, with the result that the reliability of wiring layers to be formed over the other interlayer dielectric layer can be improved.

In a method for manufacturing a semiconductor device in accordance with certain embodiments of the present invention, the following step may be added. The step (b) described above includes the step of forming a silicide wiring layer that connects to the source/drain regions of the field effect transistor. The silicide wiring layer is used, for example, to connect the source/drain of the field effect transistor to other elements. In accordance with certain embodiments of the present invention with the above-described step being added, the source/drain of the field effect transistor can be connected to the other elements without adding a wiring step.

One example of a semiconductor device manufactured in accordance with certain embodiments of the present invention is as follows. The semiconductor device described above further includes a silicide wiring layer, wherein the silicide wiring layer is connected to the source/drain of the field effect transistor, and the silicide wiring layer is located in the same layer as a silicide layer of the source/drain of the field effect transistor.

In a method for manufacturing a semiconductor device in accordance with certain embodiments of the present invention, the following step may be added. Another field effect transistor with a source/drain that does not have a silicide layer is located in the field effect transistor, and the method further includes, before the step (b), the step of (h) forming a protection layer in a region where the other field effect transistor is to be formed.

In accordance with embodiments of the present invention with the above-described step being added, a field effect transistor with its source/drain that has a silicide layer and another field effect transistor with its source/drain that does not have a silicide layer can be formed in a field effect transistor region. Depending on the use of the semiconductor device, there may be instances where the other field effect transistor is required. For example, the other field effect transistor may be used as an element that composes a peripheral circuit for a DRAM. In other words, when a DRAM macro cell (a memory cell and a peripheral circuit) and a logic circuit are mix-mounted, a silicide layer is not generally formed at source/drain of a memory cell selection field effect transistor. This is to reduce the leak current, as described above. When a DRAM macro cell is designed, using memory cells of a general-purpose DRAM, the design of the DRAM macro cell becomes easier if a silicide layer is not present at a source/drain of a transistor located in the peripheral circuit for the DRAM.

Certain embodiments of the present invention provide a method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region, a first field effect transistor that is located in a peripheral circuit region and becomes a component of a peripheral circuit for the DRAM, and a second field effect transistor located in a region other than the memory cell region and the peripheral circuit region. The method comprises the steps of: (A) forming the first field effect transistor with a source/drain that does not have a silicide layer in the peripheral circuit region; after the step (A), (B) forming a capacitor for the DRAM; and after the step (B), (C) forming a silicide layer at a source/drain of the second field effect transistor.

By the method for manufacturing a semiconductor device as described above, the capacitor for the DRAM is inhibited or prevented from being polluted by metals, and the resistance of the silicide layer formed at the source/drain of the second field effect transistor is prevented from increasing.

Also, in the method for manufacturing a semiconductor device as described above, the first field effect transistor and the second field effect transistor are formed by independent steps. As a result, the transistors can be independently optimized.

It is noted that, in embodiments of the present invention, regions other than the memory cell region and the peripheral circuit region refer to, for example, a logic circuit region.

One example of a semiconductor device manufactured in accordance with an embodiment of the present invention is as follows. Namely, the semiconductor device comprises a DRAM located in a memory cell region, a first field effect transistor that is located in a peripheral circuit region and becomes a component of a peripheral circuit for the DRAM, and a second field effect transistor located in a region other than the memory cell region and the peripheral circuit region. The semiconductor device is characterized in that silicide layers are formed at a cell plate that is a component of a capacitor of the DRAM and at a source/drain that is a component of the second field effect transistor, but silicide layers are not formed at a source/drain that is a component of a memory cell selection field effect transistor of the DRAM or at a source/drain that is a component of the first field effect transistor.

Preferred embodiments of the present invention will be described with reference to the accompanying drawings. FIG. 12 schematically shows a cross section of a semiconductor device manufactured by a method for manufacturing a semiconductor device in accordance with one embodiment of the present invention. The semiconductor device 1 includes a DRAM region 1000, a peripheral circuit region for a DRAM 2000, and a logic circuit region 3000. The semiconductor device 1 is a DRAM mixed-mount type, in which a DRAM macro cell is formed from a memory cell array formed in the DRAM region 1000 and a peripheral circuit formed in the peripheral circuit region 2000.

The DRAM region 1000 includes a word line 100, MOS (Metal Oxide Semiconductor) field effect transistors 200 a and 200 b, a bit line 300, and a capacitor 700. The MOS field effect transistors 200 a and 200 b are memory cell selection field effect transistors. The MOS field effect transistor 200 a and the capacitor 700 form one memory cell.

A MOS field effect transistor 200 c is located in the peripheral circuit region 2000. The MOS field effect transistor 200 c defines a component of a peripheral circuit for a DRAM.

MOS field effect transistors 200 d and 200 e are located in the logic circuit region 3000. The MOS field effect transistors 200 d and 200 e define components of the logic circuit.

The semiconductor device 1 generally has the structure as described above. Next, a structure of the DRAM region 1000 is described in detail. Then, a structure of the peripheral circuit region 2000, and a structure of the logic circuit region 3000 will be described in detail.

A preferred structure of the DRAM region 1000 is as follows. A P type well 13 is formed in a P⁻ type silicon substrate 11. A field oxide layer 15 a is selectively formed on the P type well 13. A region that is defined by the field oxide layer 15 a and another field oxide layer that is not shown in the figure among the P type well 13 defines an active region 13 a. The MOS field effect transistors 200 a and 200 b are formed in the active region 13 a. Also, the word line 100 is located over the field oxide layer 15 a.

First, the MOS field effect transistor 200 a is described. The MOS field effect transistor 200 a is equipped with a gate electrode (word line) 17 a, an N⁺ type source/drain region 41 a, and an N⁺ type source/drain region 41 b. The N⁺ type source/drain region 41 a and the N⁺ type source/drain region 41 b are located on the surface of the active region 13 a and spaced from each other. The gate electrode 17 a is located through a gate oxide layer 25 a over a region between the N⁺ type source/drain region 41 a and the N⁺ type source/drain region 41 b among the active region 13 a. The gate electrode 17 a has a structure having a polycrystal silicon layer 21 and a tungsten silicide layer 23 located thereon. The MOS field effect transistor 200 a has the structure described above. The MOS field effect transistor 200 b also has the structure as that of the MOS field effect transistor 200 a, and therefore a separate description of the MOS field effect transistor 200 b is omitted.

The word line 100 has a structure having a polycrystal silicon layer 21 and a tungsten silicide layer 23 located thereon.

A TEOS layer 31, a silicon nitride layer 33 and an interlayer dielectric layer 35 are successively provided in a manner to cover the MOS field effect transistors 200 a and 200 b and the word line 100. The interlayer dielectric layer 35 may be formed from, for example, a silicon oxide layer. A contact hole 37 is formed in the interlayer dielectric layer 35. The contact hole 37 reaches the N⁺ type source/drain region 41 b. The bit line 300 is located above the interlayer dielectric layer 35. The bit line 300 passes through the contact hole 37 and electrically connects to the N⁺ type source/drain region 41 b. The bit line 300 has a structure including a polycrystal silicon layer 43 and a tungsten silicide layer 45 located thereon.

An interlayer dielectric layer 47 is located in a manner to cover the bit line 300. The interlayer dielectric layer 47 may be formed from, for example, a silicon oxide layer. A contact hole 51 is formed in a layer composed of the interlayer dielectric layers 47 and 35, the silicon nitride layer 33 and the TEOS layer 31. The contact hole 51 reaches the N⁺ type source/drain region 41 a.

The capacitor 700 is located above the interlayer dielectric layer 47. The capacitor 700 includes a storage node 53, an ON layer 61 and a cell plate 67. The storage node 53 is located above the interlayer dielectric layer 47. The storage node 53 connects to the N⁺ type source/drain region 41 a through a conductive layer 58 that is filled in the contact hole 51. The storage node 53 and the conductive layer 58 are polycrystal silicon layers, and are integrally formed. The ON layer 61 is located in a manner to cover the storage node 53. The ON layer 61 is formed from a silicon oxide layer and a silicon nitride layer, and functions as a dielectric layer. The cell plate 67 is located in a manner to cover the ON layer 61. The cell plate 67 is a polycrystal silicon layer. A silicide layer 19 c is located over the cell plate 67.

An interlayer dielectric layer 71 is located in a manner to cover the capacitor 700. The interlayer dielectric layer 71 may be formed from, for example, a silicon oxide layer. A plurality of wirings, for example, aluminum wirings 75 are located above the interlayer dielectric layer 71. The detailed description of the structure of the DRAM region 1000 is completed.

A preferred structure of the peripheral circuit region 2000 is as follows. A P type well 13 is formed in a P⁻ type silicon substrate 11. A field oxide layer 15 b is selectively formed on the P type well 13. A region that is defined by the field oxide layer 15 a and the field oxide layer 15 b among the P type well 13 defines an active region 13 b. The MOS field effect transistor 200 c is formed in the active region 13 b.

The MOS field effect transistor 200 c is equipped with a gate electrode 17 c, an N⁺ type source/drain region 41 c, and an N⁺ type source/drain region 41 d. The N⁺ type source/drain region 41 c and the N⁺ type source/drain region 41 d are located on the surface of the active region 13 b and spaced from each other. Silicide layers 19 a and 19 b are located above the N⁺ type source/drain regions 41 c and 41 d, respectively. The gate electrode 17 c is located through a gate oxide layer 25 c over a region between the N⁺ type source/drain region 41 d and the N⁺ type source/drain region 41 c among the active region 13 b. The gate electrode 17 c has a structure having a polycrystal silicon layer 21 and a tungsten silicide layer 23 located thereon. Sidewalls 46 are located on both sides of the gate electrode 17 c. The sidewall 46 is formed from a silicon nitride layer 33 and a TEOS layer 31 that is located between the silicon nitride layer 33 and the gate electrode 17 c.

An interlayer dielectric layer 71 is located in a manner to cover the MOS field effect transistor 200 c. The interlayer dielectric layer 71 may be formed from, for example, a silicon oxide layer. A plurality of wirings, for example, aluminum wirings 75 are located above the interlayer dielectric layer 71.

A preferred structure of the logic circuit region 3000 is as follows. A P type well 13 is formed in a P⁻ type silicon substrate 11. Field oxide layers 15 c, 15 d and 15 e are selectively formed on the P type well 13. A region that is defined by the field oxide layer 15 c and the field oxide layer 15 d among the P type well 13 defines an active region 13 c. A region that is defined by the field oxide layer 15 d and the field oxide layer 15 e among the P type well 13 defines an active region 13 d. The MOS field effect transistors 200 d and 200 e are formed in the active regions 13 c and 13 d, respectively. The MOS field effect transistors 200 d and 200 e have the same structure as that of the MOS field effect transistor 200 c, and therefore a separate description thereof is omitted.

An interlayer dielectric layer 71 is located in a manner to cover the MOS field effect transistors 200 d and 200 e. The interlayer dielectric layer 71 may be formed from, for example, a silicon oxide layer. A plurality of wirings, for example, aluminum wirings 75 are located above the interlayer dielectric layer 71.

A method for manufacturing the semiconductor device 1 shown in FIG. 12 in accordance with an embodiment of the present invention is described with reference to FIGS. 1 through 11. FIGS. 1 through 11 show steps of the method for manufacturing the semiconductor device 1.

First, steps of forming gate electrodes 17 a and 17 c and a word line 100 shown in FIG. 12 are described with reference to FIGS. 1 and 2.

As shown in FIG. 1, field oxide layers 15 a, 15 b, 15 c, 15 d and 15 e are formed on the surface of a P⁻ type semiconductor substrate 11 by a selective oxide method, for example. The field oxide layer 15 a is formed in the DRAM region 1000. The field oxide layer 15 b is formed in the peripheral circuit region 2000. The field oxide layers 15 c, 15 d and 15 e are formed in the logic circuit region 3000.

Next, a p-type impurity (for example, boron) is ion-implanted in the surface of the P⁻ type semiconductor substrate 11, to thereby form a P type well 13 in the P⁻ type semiconductor substrate 11. Among the P type well 13, a region that is defined by the field oxide layer 15 a and another field oxide layer (not shown in the figure) becomes an active region 13 a. Also, among the P type well 13, a region that is defined by the field oxide layer 15 a and the field oxide layer 15 b becomes an active region 13 b. Also, among the P type well 13, a region that is defined by the field oxide layer 15 c and the field oxide layer 15 d becomes an active region 13 c. Also, among the P type well 13, a region that is defined by the field oxide layer 15 d and the field oxide layer 15 e becomes an active region 13 d.

As shown in FIG. 2, the P⁻ type semiconductor substrate 11 is, for example, thermally oxidized to form thermal oxide layers that become gate oxide layers 25 a and 25 c over the active regions 13 a, 13 b, 13 c and 13 d. Then, a doped amorphous silicon layer is formed on the thermal oxide layers by using, for example, a CVD method. The doped amorphous silicon layer becomes a component of a gate electrode and the like. The doped amorphous silicon layer becomes a polycrystal silicon layer 21 in a heat treatment conducted during the manufacturing process. Then, a tungsten silicide layer 23 is formed over the doped amorphous silicon layer by using, for example, a CVD method. Next, a silicon oxide layer 27 that becomes a cap layer is formed over the tungsten silicide layer 23 by, for example, a CVD method.

A structure having the thermal oxide layer, the doped amorphous silicon layer, the tungsten silicide layer 23 and the silicon oxide layer 27 is subject to a specified patterning by, for example, photolithography and etching. As a result, a word line 100 and gate electrodes 17 a are formed in the DRAM region 1000. Also, gate electrodes 17 c are formed in the peripheral circuit region 2000 and the logic circuit region 3000.

Next, an N type impurity (for example, phosphorous) is ion-implanted in the active regions 13 a, 13 b, 13 c and 13 d, using the gate electrodes 17 a and 17 c as masks, to thereby form N⁻ type impurity regions 29 a, 29 b, 29 c and 29 d.

Steps of forming a bit line 300 shown in FIG. 12 are described with reference to FIGS. 3 and 4.

As shown in FIG. 3, a TEOS layer 31 is formed in a manner to cover the P⁻ type semiconductor substrate 11 by, for example, a CVD method. Then, a silicon nitride layer 33 is formed over the TEOS layer 31 by, for example, a CVD method. The TEOS layer 31 and the silicon nitride layer 33 function as an etching stopper in the succeeding steps, i.e., the step of forming a contact hole and the step of removing an interlayer dielectric layer.

As shown in FIG. 4, an interlayer dielectric layer 35 that is composed of a silicon oxide layer is formed over the silicon nitride layer 33 by, for example, a CVD method. Then, a resist is formed over the interlayer dielectric layer 35. A layer composed of the interlayer dielectric layer 35, the silicon nitride layer 33 and the TEOS layer 31 is selectively etched, using the resist as a mask, to form a contact hole 37 that reaches the N⁻ type impurity region 29 b. The step of forming the contact hole 37 is described in detail below.

In the step of forming the contact hole 37, first, the interlayer dielectric layer 35 is etched with the resist functioning as a mask. In this etching step, the silicon nitride layer 33 functions as an etching stopper. After the resist is removed, the silicon nitride layer 33 is etched. In this etching step, the TEOS layer 31 functions as an etching stopper. Then, lastly, the TEOS layer 31 is etched. By the steps described above, the contact hole 37 is formed in a self-alignment manner. By forming the contact hole 37 in this manner, the gate electrode 17 a is prevented from being exposed through the contact hole 37. Then, an N type impurity (for example, phosphorous) is ion-implanted in the active region 13 a, using the interlayer dielectric layer 35 as a mask, to form an N⁺ type impurity region 39. The N⁺ type impurity region 39 and the N⁻ type impurity region 29 b form an N⁺ type source/drain region 41 b.

Next, a doped amorphous silicon layer is formed on the interlayer dielectric layer 35 by using, for example, a CVD method. The doped amorphous silicon layer becomes a silicon layer 43 that is a component of the bit line. The doped amorphous silicon layer becomes a polycrystal silicon layer 43 in a heat treatment conducted during the manufacturing process. Then, a tungsten silicide layer 45 is formed over the doped amorphous silicon layer by using, for example, a CVD method. A structure composed of the doped amorphous silicon layer and the tungsten silicide layer 45 is subject to a specified patterning by, for example, photolithography and etching. As a result, a bit line 300 is formed in the DRAM region 1000. The bit line 300 is also formed on the inside of the contact hole 37 and electrically connects to the N⁺ type source/drain region 41 b.

Steps of forming a doped polycrystal silicon layer that becomes a storage node 53 and a cell plate 67 shown in FIG. 12 are described with reference to FIGS. 5 and 6.

As shown in FIG. 5, an interlayer dielectric layer 47 that is composed of a silicon oxide layer is formed over the surface of the P⁻ type semiconductor substrate 11 in a manner to cover the bit line 300 by, for example, a CVD method. Then, a resist is formed over the interlayer dielectric layer 47. A layer composed of the interlayer dielectric layers 47 and 35, the silicon nitride layer 33 and the TEOS layer 31 is selectively etched, using the resist as a mask, to form a contact hole 51. The contact hole 51 reaches the N⁻ type impurity region 29 a.

Then, an N type impurity (for example, phosphorous) is ion-implanted in the active region 13 a, using the interlayer dielectric layer 47 as a mask, to form an N⁺ type impurity region 49. The N⁺ type impurity region 49 and the N⁻ type impurity region 29 a form an N⁺ type source/drain region 41 a.

Then, a doped amorphous silicon layer is formed over the interlayer dielectric layer 47 and on the inside of the contact hole 51 by, for example, a CVD method. The doped amorphous silicon layer over the interlayer dielectric layer 47 becomes a storage node. The doped amorphous silicon layer inside the contact hole 51 becomes a conductive layer 58. The doped amorphous silicon layer becomes a silicon layer having a polycrystal structure in a heat treatment conducted during the manufacturing process.

Next, the doped amorphous silicon layer is subject to a specified patterning by, for example, photolithography and etching. As a result, a storage node 53 is formed in the DRAM region 1000. The surface of the storage node 53 is preferably roughened by a known method. As a result, the surface area of the storage node 53 becomes greater, which increases the storage capacity of the capacitor.

Then, as shown in FIG. 6, a silicon nitride layer is formed in a manner to cover the storage node 53 over the surface of the P⁻ type semiconductor substrate 11 by, for example, a CVD method. This may be conducted, for example, at a temperature of 650° C. for 15 minutes. The silicon nitride layer is thermally oxidized to form a silicon oxide layer on the surface of the silicon nitride layer, which define an ON layer 61. The thermal oxidation may be conducted, for example, at a temperature of 820° C. for 13 minutes.

Then, a doped polycrystal silicon layer 63 that becomes a cell plate is formed in a manner to cover the ON layer 61 over the surface of the P⁻ type semiconductor substrate 11 by, for example, a CVD method.

Steps of forming MOS field effect transistors 200 c, 200 d and 200 e shown in FIG. 12 are described with reference to FIGS. 7 through 9.

As shown in FIG. 7, a resist 59 is formed over the surface of the P⁻ type semiconductor substrate 11. Then, the resist 59 is selectively removed in a manner to leave the resist 59 over the doped polycrystal silicon layer 63 that is located in the DRAM region 1000.

Then, the doped polycrystal silicon layer 63, the ON layer 61, the interlayer dielectric layer 47 and the interlayer dielectric layer 35 are successively etched and removed, using the resist 59 as a mask. In this step, since the silicon nitride layer 33 has a different etching rate from that of the interlayer dielectric layer 35 (silicon oxide layer), the silicon nitride layer 33 functions as an etching stopper. In this case, when the interlayer dielectric layer 47 and the interlayer dielectric layer 35 are removed by a wet etching method, for example, using HF, the silicon nitride layer 33 can securely function as an etching stopper layer. The interlayer dielectric layers 47 and 35 can also be removed by a dry etching method. It is noted that the doped polycrystal silicon layer 63 that remains in the DRAM region 1000 becomes a cell plate 67.

As shown in FIG. 8, the silicon nitride layer 33 and the TEOS layer 31 that are located in the peripheral circuit region 2000 and the logic circuit region 3000 are successively etched across their surfaces, to thereby form sidewalls 46 on side walls of the gate electrode 17 c. Then, the resist 59 is removed.

Then, an N type impurity (for example, phosphorous) is ion-implanted in the active regions 13 b, 13 c and 13 d, using the sidewalls 46 and the gate electrode 17 c as masks, to form an N⁺ type impurity region 54. The N⁺ type impurity region 54 and the N⁻ type impurity region 29 c form an N⁺ type source/drain region 41 c. Also, the N⁺ type impurity region 54 and the N⁻ type impurity region 29 d form an N⁺ type source/drain region 41 d.

As shown in FIG. 9, a titanium layer is formed over the surface of the P⁻ type semiconductor substrate 11. Then, the titanium layer is subject to a first thermal treatment in, for example, a nitrogen atmosphere. As a result, a silicide layer of titanium is formed. Then, the titanium nitride layer and non-reacted portions of the titanium layer are removed by, for example, a wet etching method. As a result, silicide layers 19 a, 19 b and 19 c are left over the N⁺ type source/drain region 41 c, the N⁺ type source/drain region 41 d and the cell plate 67, respectively. Then, for example, a second heat treatment is conducted. By the second heat treatment, the silicide layers 19 a, 19 b and 19 c undergo a phase transition from a high resistance crystal structure (C49 structure) to a low resistance crystal structure (C54 structure).

As shown in FIG. 10, an interlayer dielectric layer 71 that is composed of a silicon oxide layer is formed over the surface of the P⁻ type semiconductor substrate 11 in a manner to cover the capacitor 700 and the MOS field effect transistors 200 c, 200 d and 200 e by, for example, a CVD method. A step 62 is formed in the interlayer dielectric layer 71 at a border between the DRAM region 1000 and the peripheral circuit region 2000. The step 62 is created due to differences in the device density, the number of interlayer dielectric layers and the like.

Then, as shown in FIG. 11, the interlayer dielectric layer 71 is preferably polished by a CMP method for three minutes using a slurry containing silica in a NH₃ based solution and a polishing pad, to thereby planarize the interlayer dielectric layer 71.

Then, as shown in FIG. 12, a plurality of wirings such as, for example, aluminum wirings 75 are formed over the interlayer dielectric layer 71 by a known method.

By the manufacturing steps described above, the semiconductor device 1 shown in FIG. 12 is completed. By using a preferred method for manufacturing the semiconductor device 1, the following effects are preferably created.

First, in accordance with certain embodiments of the present invention, after the capacitor 700 of the DRAM is formed, the silicide layers 19 a and 19 b are formed over the N⁺ type source/drain regions 41 c and 41 d of the MOS field effect transistors 200 c, 200 d and 200 e. Therefore, the capacitor 700 is inhibited of prevented from being polluted with metals. Accordingly, in accordance with one embodiment of the present invention, the characteristic of the capacitor of the DRAM can be inhibited or prevented from being deteriorated.

Second, in accordance with certain embodiments of the present invention, after the capacitor 700 of the DRAM is formed, the silicide layers 19 a and 19 b are formed over the N⁺ type source/drain regions 41 c and 41 d of the MOS field effect transistors 200 c, 200 d and 200 e. As a result, the silicide layers 19 a and 19 b should not be significantly affected by heat, and therefore the resistance of the silicide layers 19 a and 19 b can be inhibited or prevented from increasing. It is noted that the heat mentioned above refers to the heat that is used in the step of thermally oxidizing a silicon nitride layer in the formation of the ON layer 61 (at 820° C., as described above with reference to FIG. 6) and in the steps of forming the interlayer dielectric layers 35 and 47 (over 800° C.).

Third, in accordance with certain embodiments of the present invention, after the capacitor 700 is formed, the MOS field effect transistors 200 c, 200 d and 200 e are formed. Accordingly, as shown in FIG. 7, the doped polycrystal silicon layer 63, the ON layer 61, the interlayer dielectric layer 47 and the interlayer dielectric layer 35 need to be successively etched and removed, using the resist 59 as a mask. In accordance with one embodiment of the present invention, the silicon nitride layer 33 is formed below the interlayer dielectric layer (silicon oxide layer) 35. Since the silicon nitride layer 33 has an etching rate different from those of the interlayer dielectric layer 47 and the interlayer dielectric layer 35 (silicon oxide layer), the silicon nitride layer 33 functions as an etching stopper, when the etching and removal step described above is conducted. As a result, when the interlayer dielectric layers 47 and 35 are etched and removed, an underlying layer such as a field oxide layer is prevented from being etched at areas where the thickness of the interlayer dielectric layer (in this case, the interlayer dielectric layer 35 and the interlayer dielectric layer 47 are considered to be one interlayer dielectric layer) is small. Therefore, the occurrence of problems, such as, for example, a lowered element isolation dielectric strength and the like, is inhibited or prevented.

Fourth, as shown in FIG. 11, in accordance with one embodiment of the present invention, the interlayer dielectric layer 71 is planarized by a CMP method. As a result, the reliability of the aluminum wirings 75 can be improved.

The embodiments of the present invention have a variety of modifications. Certain modified embodiments will be described below.

FIG. 13 shows the planarization step for the interlayer dielectric layer 71 in accordance with a modified embodiment of the present invention. In this modified embodiment, initially, a resist 65 is formed over the surface of the interlayer dielectric layer 71. Then, the resist 65 is selectively exposed to light and developed to remove the resist 65 that is located over the DRAM region 1000. As a result, the resist 65 remains on the interlayer dielectric layer 71 at areas located above the peripheral circuit region 2000 and the logic circuit region 3000. Then, the interlayer dielectric layer 71 located above the DRAM region 1000 is etched, using the resist 65 as a mask, to planarize the interlayer dielectric layer 71.

FIG. 14 shows a step of forming a silicide wiring layer 19 d in accordance with another modified embodiment. The silicide wiring layer 19 d is located above the field oxide layer 15 d. The silicide wiring layer 19 d connects the N⁺ type source/drain region 41 c of the MOS field effect transistor 200 e to the N⁺ type source/drain region 41 d of the MOS field effect transistor 200 d.

Steps of forming the silicide wiring layer 19 d are described. First, a titanium silicide layer is formed over the surface of the P⁻ type semiconductor substrate 11. Then, the silicide layer is selectively removed by, for example, photolithography and etching, to form the silicide layers 19 a, 19 b, 19 c and 19 d.

In accordance with the modified embodiment described above, the N⁺ type source/drain region 41 c of the MOS field effect transistor 200 e can be connected to the N⁺ type source/drain region 41 d of the MOS field effect transistor 200 d, without adding steps of forming wiring layers.

FIG. 15 is an illustration to describe steps of selectively forming a silicide layer in accordance with another modified embodiment. First, after the step shown in FIG. 8, a protection layer 77 is formed over the surface of the P⁻ type semiconductor substrate 11, as shown in FIG. 15. The protection layer 77 may be formed from, for example, a silicon oxide layer. The protection layer 77 is selectively removed by, for example, photolithography and etching. As a result, the protection layer 77 remains in the DRAM region 1000 and the peripheral circuit region 2000. The protection layer 77 does not remain in the logic circuit region 3000. Then, when the silicide layer forming step described with reference to FIG. 9 is conducted, the silicide layers 19 a and 19 b are formed only in the logic circuit region 3000, as shown in FIG. 15.

A silicide layer is not formed at the source/drain of the MOS field effect transistor 200 c in the peripheral circuit region 2000 because of the following reasons. When a DRAM macro cell (a memory cell and a peripheral circuit) and a logic circuit are mix-mounted, a silicide layer is not formed at a source/drain of the MOS field effect transistor in the DRAM region 1000. This is to reduce the leak current. When a DRAM macro cell is designed, using memory cells of a general-purpose DRAM, the design of the DRAM macro cell becomes easier if a silicide layer is not present at the source/drain of the MOS field effect transistor located in the peripheral circuit region 2000.

In another modified embodiment, a MOS field effect transistor located in the peripheral circuit region 2000 and a MOS field effect transistor located in the logic circuit region 3000 are formed independently from each other. This embodiment is described below.

After the step shown in FIG. 3, a resist 89 is formed over the surface of the silicon nitride layer 33, as shown in FIG. 16. Then, the resist 89 is selectively exposed to light and developed, to remove the resist 89 located above the peripheral circuit region 2000. As a result, the resist 89 located above the DRAM region 1000 and the logic circuit region 3000 remains. Then, the silicon nitride layer 33 and the TEOS layer 31 located above the peripheral circuit region 2000 are etched, using the resist 89 as a mask, to form sidewalls 46 on both sides of the gate electrode 17 c.

Then, an N type impurity (for example, phosphorous) is ion-implanted in the active region 13 b, using the sidewalls 46, the gate electrode 17 c and the resist 89 as masks, to form an N⁺ type impurity region 54. The N⁺ type impurity region 54 and the N⁻ type impurity region 29 c form an N⁺ type source/drain region 41 c. Also, the N⁺ type impurity region 54 and the N⁻ type impurity region 29 d form an N⁺ type source/drain region 41 d. By the steps described above, the MOS field effect transistor 200 c located in the peripheral circuit region 2000 is completed.

Then, steps are conducted until a doped polycrystal silicon layer 63 shown in FIG. 6 is formed.

Then, as shown in FIG. 17, a resist 91 is formed in the DRAM region 1000. The doped polycrystal silicon layer 63 and the ON layer 61 are selectively etched, using the resist 91 as a mask. As a result, a cell plate 67 is formed, and the doped polycrystal silicon layer 63 and the ON layer 61 are removed from the peripheral circuit region 2000 and the logic circuit region 3000.

Next, as shown in FIG. 18, a resist 93 is formed in the DRAM region 1000 and the peripheral circuit region 2000. The interlayer dielectric layer 47 and the interlayer dielectric layer 35 located in the logic circuit region 3000 are successively etched and removed. In this step, since the silicon nitride layer 33 has a different etching rate than that of the interlayer dielectric layer 35 (silicon oxide layer), the silicon nitride layer 33 functions as an etching stopper.

Then, as shown in FIG. 19, the MOS field effect transistors 200 d and 200 e located in the logic circuit region 3000 are completed. These steps are the same as the steps described with reference to FIG. 8 and FIG. 9.

In accordance with this modified embodiment, the MOS field effect transistors 200 d and 200 e formed in the logic circuit region 3000 are formed independently of the steps for forming the MOS field effect transistor 200 c that is formed in the peripheral circuit region 2000. As a result, the respective transistors can be optimized.

While the description above refers to particular embodiments of the present invention, it will be understood that many modifications may be made without departing from the spirit thereof The accompanying claims are intended to cover modifications that fall within the true scope and spirit of the present invention. 

What is claimed:
 1. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; (b) after the step (a), forming a silicide layer at a source/drain region of the field effect transistor; and (c) after the step (b), the steps of: (c1) forming an additional interlayer dielectric layer in the memory cell region and the field effect transistor region; and (c2) polishing the additional interlayer dielectric layer by CMP to thereby planarize the additional interlayer dielectric layer.
 2. A method for manufacturing a semiconductor device according to claim 1, the method further comprising the steps of: (d) before the step (a), the steps of: (d1) forming an etching stopper layer in the field effect transistor region; and (d2) forming an interlayer dielectric layer in the memory cell region and the field effect transistor region; and (e) between the step (a) and the step (b), the step of removing the interlayer dielectric layer located in the field effect transistor region by an etching, using the etching stopper layer as an etching stopper.
 3. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; (b) after the step (a), forming a silicide layer at a source/drain region of the field effect transistor; and (c) after the step (b), the steps of: (c1) forming an additional interlayer dielectric layer in the memory cell region and the field effect transistor region; and (c2) photo-etching the additional interlayer dielectric layer located in the memory cell region to thereby planarize the additional interlayer dielectric layer.
 4. A method for manufacturing a semiconductor device as in claim 3, the method further comprising the steps of: (d) before the step (a), the steps of: (d1) forming an etching stopper layer in the field effect transistor region; and (d2) forming an interlayer dielectric layer in the memory cell region and the field effect transistor region; and (e) between the step (a) and the step (b), the step of removing the interlayer dielectric layer located in the field effect transistor region by an etching, using the etching stopper layer as an etching stopper.
 5. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; (b) after the step (a), forming a silicide layer at a source/drain region of the field effect transistor; and wherein the step (b) also includes the step of forming a silicide wiring layer that connects to the source/drain region of the field effect transistor.
 6. A method for manufacturing a semiconductor device as in claim 5, (c) before the step (a), the steps of (c1) forming an etching stopper layer in the field effect transistor region; and (c2) forming an interlayer dielectric layer in the memory cell region and the field effect transistor region; and (d) between the step (a) and the step (b), the step of removing the interlayer dielectric layer located in the field effect transistor region by an etching, using the etching stopper layer as an etching stopper.
 7. A method for manufacturing a semiconductor device according to claim 1, wherein the step (b) includes the step of forming a silicide wiring layer that connects to the source/drain region of the field effect transistor.
 8. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; (b) after the step (a), forming a silicide layer at a source/drain region of the field effect transistor; and (c) wherein an additional field effect transistor with a source/drain that does not have a silicide layer is formed in the semiconductor device, and, before the step (b), the step of forming a protection layer in a region where the additional field effect transistor is to be formed.
 9. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region and a field effect transistor located in a field effect transistor region that is a region other than the memory cell region, the method comprising the steps of: (a) forming a capacitor for the DRAM; (b) after the step (a), forming a silicide layer at a source/drain region of the field effect transistor; (c) before the step (a), the steps of: (c1) forming an etching stopper layer in the field effect transistor region; and (c2) forming an interlayer dielectric layer in the memory cell region and the field effect transistor region; (d) between the step (a) and the step (b), the step of removing the interlayer dielectric layer located in the field effect transistor region by an etching, using the etching stopper layer as an etching stopper; and (e) wherein an additional field effect transistor with a source/drain that does not have a silicide layer is formed in the semiconductor device and, before the step (b), the step of forming a protection layer in a region where the additional field effect transistor is to be formed.
 10. A method for manufacturing a semiconductor device according to claim 1, wherein an additional field effect transistor with a source/drain that does not have a silicide layer is formed in the semiconductor device, and further comprising, before the step (b), the step of forming a protection layer in a region where the additional field effect transistor is to be formed.
 11. A method for manufacturing a semiconductor device according to claim 5, wherein an additional field effect transistor with a source/drain that does not have a silicide layer is formed in the semiconductor device, and further comprising, before the step (b), the step of forming a protection layer in a region where the additional field effect transistor is to be formed.
 12. A method for manufacturing a semiconductor device, the semiconductor device having a DRAM located in a memory cell region, a first field effect transistor that is located in a peripheral circuit region and becomes a component of a peripheral circuit for the DRAM, and a second field effect transistor located in a region other than the memory cell region and the peripheral circuit region, the method comprising the steps of: (A) forming the first field effect transistor with a source/drain that does not have a silicide layer in the peripheral circuit region; (B) after the step (A), forming a capacitor for the DRAM; and (C) after the step (B), forming a silicide layer at a source/drain of the second field effect transistor.
 13. A method for manufacturing a semiconductor device, the semiconductor device having a substrate that includes a memory cell region and a field effect transistor region, a RAM located in the memory cell region and a field effect transistor located in the field effect transistor region, the method comprising the steps of: (a) forming a capacitor for the RAM in the memory cell region; and (b) after step (a), forming a silicide layer at a source/drain region of the field effect transistor and on the capacitor.
 14. A method for manufacturing a semiconductor device, the semiconductor device having a substrate that includes a memory cell region and a field effect transistor region, a RAM located in the memory cell region and a field effect transistor located in the field effect transistor region, the method comprising the steps of: forming a gate electrode located in the field effect transistor region; forming a dielectric layer in the field effect transistor region; forming an interlayer dielectric layer in the memory cell region and the field effect transistor region, the interlayer dielectric layer formed from a material having a different etching rate from that of the dielectric layer; forming a capacitor for the RAM; removing the interlayer dielectric layer located in the field effect transistor region by an etching using the dielectric layer as an etching stopper; and forming a sidewall located on side wall of the gate electrode by etching the dielectric layer.
 15. A method for manufacturing a semiconductor device, the semiconductor device having a substrate that includes a memory cell region and a field effect transistor region, a RAM located in the memory cell region and a field effect transistor located in the field effect transistor region, the method comprising the steps of: forming a gate electrode located in the field effect transistor region; forming a first dielectric layer in the field effect transistor region; forming a second dielectric layer on the first dielectric layer; forming an interlayer dielectric layer in the memory cell region and the field effect transistor region, the interlayer dielectric layer being formed from a material having a different etching rate from that of the first dielectric layer; forming a capacitor for the RAM; removing the interlayer dielectric layer located in the field effect transistor region by an etching using the second dielectric layer as an etching stopper; and forming a sidewall located on side wall of the gate electrode by etching the first and second dielectric layers. 